Ceramic coatings were fabricated on AZ91D Mg-alloy substrate by microarc oxidation in Na₂SiO₃–NaOH–Na₂EDTA electrolytes with and without C₃H₈O₃ addition. The effects of different concentrations of C₃H₈O₃ contained in the electrolyte on coatings thickness were investigated. The surface morphologies, RMS roughness, phase compositions and corrosion resistance property of the ceramic coatings were analyzed by scanning electron microscopy (SEM), atomic force microscopy (AFM), X-ray diffraction (XRD), and electrochemical corrosion test respectively. It is found that the addition of C₃H₈O₃ into silicate electrolyte leads to increase of the unit-area adsorptive capacity of the negative ions at anode–electrolyte interface and thus improves the compactness and corrosion resistance of the MAO coating. The coating thickness decreases gradually with the increase of concentrations of C₃H₈O₃ in the electrolyte. The oxide coating formed in base electrolyte containing 4 mL/L C₃H₈O₃ exhibits the best surface appearance, the lowest surface RMS roughness (174 nm) and highest corrosion resistance. In addition, both ceramic coatings treated in base electrolyte with and without C₃H₈O₃ are mainly composed of periclase MgO and forsterite Mg₂SiO₄ phase, but no diffraction peak of Mg phase is found in the patterns.