ZrO2/PMMA nanocomposite particles are synthesized through an in-situ free radical emulsion polymerization based on the silane coupling agent (Z-6030) modified ZrO2 nanoparticles, and the morphology, size and its distribution of nanocomposite particles are investigated. Scanning electron microscopy (SEM) images demonstrate that the methyl methacrylate (MMA) feeding rate has a significant effect on the particle size and morphology. When the MMA feeding rate decreases from 0.42mlmin-1 to 0.08mlmin-1, large particles (about 200-550nm) will not form, and the size distribution become narrow (36-54nm). The average nanocomposite particles size increases from 34nm to 55nm, as the MMA/ZrO2 nanoparticles mass ratio increased from 4:1 to 16:1. Regular spherical ZrO2/PMMA nanocomposite particles are synthesized when the emulsifier OP-10 concentration is 2mgml-1. The nanocomposite particles could be mixed with VAc-VeoVa10 polymer matrix just by magnetic stirring to prepare the ZrO2 /PMMA/VAc-VeoVa10 hybrid coatings. SEM and atomic force microscopy (AFM) photos reveal that the distribution of the ZrO2/PMMA nanocomposite particles in the VAc-VeoVa10 polymer matrix is homogenous and stable. Here, the grafted-PMMA polymer on ZrO2 nanoparticles plays as a bridge which effectively connects the ZrO2 nanoparticles and the VAc-VeoVa10 polymer matrix with improved comparability. In consequence, the hybrid coating with good dispersion stability is obtained.

影响因子
1.174
论文下载
作者

Fangqiang FAN,Zhengbin XIA,Qingying LI,Zhong LI,Huanqin CHEN.

期刊

Chinese Journal of Chemical Engineering,21(2),113-120(2013)

年份